TABLEAU DE RÉSISTANCE DES NUANCES D'ACIER DE STRUCTURE

Tableau centré des nuances d'acier

Niveau	Résistance au rendement	Résistance ultime force	Élongation min pendant 2"	Remarques
ACIER DE CONSTRUCTION CSA G40.21
44 / 300W	44,000 PSI (304 MPA) MIN	65,000-85,000 PSI (448‑586 MPA)	23%
50 / 350W	50,000 PSI (345 MPA) MIN	65,000-90,000 PSI (448‑621 MPA)	22%
A36	36,300 PSI (250 MPA) MIN.	58,000-79,800 PSI (400‑500 MPA)	23%
4140	105,000 PSI (724 MPA) MIN	125,000 PSI (852 MPA) MIN	16%	Traité thermiquement selon la norme ASTM A193 B7
TOUTES LES TIGES FILETÉES
ASTM A307 GR. A	-	60,000 PSI (414 MPA) MIN.	18%
ASTM A193 B7	105,000 PSI (724 MPA) MIN.	125,000 PSI (852 MPA) MIN.	16%
ASTM F593 ‑CLASSE 304 / 316	Diamètre ¼‑⅝: 65,000 PSI (448 MPA) MIN. Diamètre ¾‑1 ½: 45,000 PSI (310 MPA) MIN	Diamètre ¼‑⅝: 100‑150 k PSI (689‑1035 MPA) Diamètre ¾‑1 ½: 85‑140 k PSI (586‑965 MPA)	-	Fourni CW1/CW2 sauf spécification. Même résistance pour SS304 et SS316
TIGES D'ANCRAGE
F1554 GR. 36	36,000 PSI (248 MPA) MIN.	58,000-80,000 PSI (400-552 MPA)	23%
F1554 GR. 55	55,000 PSI (379 MPA) MIN.	75,000-95,000 PSI (517-655 MPA)	21%	Alternative soudable populaire : GR. 55‑S1
F1554 GR. 105	105,000 PSI (724 MPA) MIN.	125,000-150,000 PSI (861-1034 MPA)	15%
BOULONS DE STRUCTURE ASTM F3125
GRADE A325/F1852	92,000 PSI (635 MPA) MIN.	120,000 PSI (828 MPA) MIN.	14%	Type 1 et 3 (altération) même résistance.
GRADE A490/F2280	130,000 PSI (896 MPA) MIN.	150,000 PSI (1034 MPA) MIN.	14%	Type 1 et 3 (altération) même résistance.
SAE J429
Grade 2	Diamètre ¼‑¾ : 57,000 PSI (393 MPA) MIN. Diamètre ¾‑1 ½: 36,000 PSI (248 MPA) MIN.	Diamètre ¼‑¾ : 74,000 PSI (510 MPA) MIN. Diamètre ¾‑1 ½: 60,000 PSI (414 MPA) MIN.	18%
Grade 5	Diamètre ¼‑1: 92,000 PSI (635 MPA) MIN. Diamètre 1 ⅛‑2: 81,000 PSI (558 MPA) MIN.	Diamètre ¼‑1: 120,000 PSI (830 MPA) MIN. Diamètre 1 ⅛‑2: 105,000 PSI (724 MPA) MIN	14%
Grade 8	120,000 PSI (830 MPA) MIN.	150,000 PSI (1034 MPA) MIN.	12%